surface treating agent

The surface treating agent for rubber shoe sole was synthesized by grafting modification of CR / SBS with methyl methacrylate and acrylic acid . This method solved the problem of lower adhesion strength of the conventional rubber shoe sole .

采用甲基丙烯酸甲酯、丙烯酸接枝改性CR/SBS，合成橡胶鞋底表面处理剂，解决了传统橡胶鞋底粘接强度不大等问题。

The experiments found that the finished products can meet the requirements of specification GB 9331-88 and IEC-502 ( 1994 ) by adopting 180 mesh of magnisium hydroxide as flame retardant and zinc stearate as surface treating agent especially , Both of the social and economic efficiency are higher .

试验发现，宜采用180目的氢氧化镁作阻燃剂，硬酯酸锌作表面处理剂。成品电缆性能可满足IEC502（1994）及GB933188的技术规范，且具有良好的经济和社会效益。

The nano-CaCO_3 was modified with a special surface treating agent via water phase .

在水相中对纳米碳酸钙悬浮液进行了湿法改性。

GF surface treating agent content is1 % , and the lubricating agent content is0 .

玻纤外露改性剂用量为1%，润滑剂用量为0。

The results showed , when the coupling agents content is 0.4 % . GF surface treating agent content is 1 % , and the lubricating agent content is 0.5 % , the reinforced PA6 of 60 % GF with high performance is prepared .

结果表明，偶联剂用量为0.4%，玻纤外露改性剂用量为1%，润滑剂用量为0.5%时，可以制得玻纤含量为60%的高性能的PA6增强材料。

Azeotropic distillation method was applied to the organic surface modification of nanosized alumina using lauric acid as surface treating agent .

以月桂酸为表面处理剂，采用共沸蒸馏的方法对纳米氧化铝进行了有机表面修饰。